Journeyman Welding Approaches For TIG Welding Thin Wall Stainless Pipe

Prior to starting I actually do am getting at there are hardly any locations that provides you with the opportunity to learn to TIG weld thin wall stainless pipe. I had been fortunate enough to have Fluor train me and am very grateful for having the ability to attend their training course! Fluor may be the only reason I acquired to understand this skill!

Things I can share is the fact that TIG welding stainless pipe isn’t more difficult than carbon steel pipe. There’s a couple of rules to follow along with and also you will be able to get it rapidly! The guidelines are listed below:

Purge your pipe well.

Everything should be clean.

Keep the tungsten moving whatsoever occasions.

Permit the pipe to awesome prior to the next weld.

Stainless pipe should always be purged. The end result from the under perfect purge may cause the main to obtain contaminated. The slang expression used within the field for root contamination or oxidization is “sugar”. Sugar is from the weld being uncovered to oxygen within the atmosphere. The weld joint should be recorded off and just untapped when you’re prepared to weld that part when the pipe.

Generally TIG welding needs a very clean weld joint however with stainless it is really an absolute must! The tungsten should be clean. Which means cleaning it after every restart and pass. The weld joint should be filed before every pass except the main pass. The bevel must be filed around the hot pass and all sorts of color changes have to be filed to pure metal whatsoever occasions. Failure to file for all heat impacted areas can lead to the filler wire the inability to flow in to the joint easily.

Moving your tungsten rapidly is essential when TIG welding stainless pipe. The secret to prevent melt through and overheating the pipe would be to move rapidly. As soon as you strike the arc that tungsten must be moving. Don’t start and wait for a metal to warm up before moving. Ideally you need to start 3/4 inch prior to the company will begin adding filler wire too. This allows enough preheat for that filler wire to circulate correctly. Ideally once the weld is completed it ought to possess a copper color into it. If it’s grey or dark anyway you use an excessive amount of heat or moving not fast enough!

With regards to stainless heat this metal absorbs and holds is unbelievable. Now add thin wall pipe towards the picture and you’ve got a radiator that’s always prepared to overheat! You have to permit the pipe to awesome enough that you can to the touch it together with your bare hands. TIG welding stainless pipe requires lots of awaiting the pipe to awesome. It takes only an additional inch of weld too early to ruin the weld joint!